sodium lignosulphonate concrete admixture superplasticizer - HRSC-H

1 Naphthalene-based Superplasticizer, 2 High effective water reducing rate: more than 18%, 3,Sample available - details see: https://www.buildingsupplieshub.com/sodium-lignosulphonate-concrete-admixture-superplasticizer-10082295
Place of Origin: Shandong China (Mainland)Brand Name: HRSCModel Number: HRSC-H 
sodium lignosulphonate concrete admixture superplasticizer
contact supplier for sodium lignosulphonate concrete admixture superplasticizer


It is a high range water reducer, high concentration naphthalene-based superplasticizer, also named Naphthalene Sulfonate Formaldehyde Condensate (NSF), SNF, PNS and FDN etc. NX-01NP (Na2SO4 less 5%) contains no chloride, non-corrosive to steel bars, non-poisonous, odorless, and non-flammable. Thus, it meets the requirements of chemical admixture specifications for concrete: comply with ASTM C 494, Type F. ASTM C 1017, GB8076-2008 and GB50119-2003 etc.

Naphthalene Based Superplasticizer Uses
  • It possesses the features of no retarding, no air-introducing, superplastic high water-reducing and strength enhancing. It has no chloride, low alkali content, low sulphonate, and high purity. It can be widely used in different concretes with less dosage and easy to use.
  • It can be applied to make flowing, strong or steam-curing concrete. The minimum working temperature can be as low as 0°Cdegrees. In steam curing, concrete with superplasticizer has to be strong enough before heating. The steam curing specification has to be pre-tested. It is particularly used as base material for compound admixtures.
  • It can prevent from the alkali-aggregate reaction because of the biggish alkali reactivity of aggregate or the alkali-aggregate reaction in the moist environment.

Naphthalene Based Superplasticizer

Specifications

ItemsCriteriaActual results(C×0.75%)
Appearance--Light brown powder
Solid Content %92 min92.65
Moisture %8.0 max7.35
Fineness (0.315mm remains) %15.0 max9.2
PH value7 - 98.5
Sodium Sulfate Content %5.0 max3.8
Chloride Content %1.0 max0.11
Surface Tension68-72 Mn/m71
Cement Flowing Rate240mm265mm
Water Reducing Rate20% min22.3%
Steel-bar CorrosionNoneNone

Advantage

  1. High water-reducing rate: It can reduce water 20-30%. It has features of superplasticizer, effectively increases concrete fluidity and reduces water penetration and segregation and improves the encapsulation force of the concrete with reinforcing steel bar.
  2. Strengthening: Given the same amount of cement and slump requirement, this product with the dosage 0.5-1.2% can increase the concrete early strength and reinforced effect by 50-100%, 40-70%, 25-60% and 20-60% on day 1, 3, 7, and 28 respectively.
  3. High applicability: It can be used with different variety of cement. It is compatible with other admixtures.
  4. Low sodium Sulfate content: The aqueous solution has no crystals in winter, which can avoid pipeline congestions when JK-01 NP applied. It is suitable for automatic working.
  5. Effective durability: It can modify the structure of concrete and increase the property of anti-seepage, anti-freezing, and carbonization.
Dosage
0.5-1.2% by weight of cement. Exact dosage rates are dependent on the type of effect sought, quality of cement and aggregates, water/cement ratio and ambient temperature. Therefore, in many cases it is advisable to carry out trial mixes.
It can be added directly or added in after dissolved in water. It can be added during mixing and after-mixing (better). The after-mixing approach can achieve better result.
Packaging Detail:Woven plastic bag with film liner. Net weight: 25kg/40kg