Single pack polyurethane waterproof coating(E-929) - E-929

1.One-component packaging, it can be used once opening., 2.Reliable performance., 3.Environment friendly. - details see: https://www.buildingsupplieshub.com/single-pack-polyurethane-waterproof-coating-e-929-10100422

Type: Other Waterproofing Materials	Place of Origin: Guangdong China (Mainland)	Brand Name: Elokt	Model Number: E-929
Solid Contained: more than 80%	Usage: Non-exposed roof, underground , kitchen , bath	Certificate: ISO	Application Method: Brush
Elongation at break: 450-550%	Main Raw Material: Polyurethane	Shelf Life: 12 months	Consumption: 1.3kg/㎡ when the thickness of coating is 1 mm
Color: White

Single Pack Polyurethane Waterproof CoatingE-929

Product mechanism

The reaction mechanism of E- 929 is that the NCO end group of the PUP touches air or the tidal air of the basement layer that they solidify into films, it can construct in moist base course and complicated projects. There will be a seamless, strong bonding, stretchy and tough waterproof film.

Product features

1.One-component packaging, it can be used once opening.

2.Reliable performance.

3.Environment friendly: accord with the harmful substances stander GB 50325-2001

4.Complex use withhigh polymer membrane, self-adhesive polymer modified-bitumen waterproof membrane.

Applicable scope

Non-exposed roof, underground waterproofing, kitchen & bath and non-drinking water project

Performance index

No.	Item		I	II
1	Tensile strength (Mpa) ≥		1.9	2.45
2	Eongation at break % ≥		550	450
3	Tear strength(N/mm) N/mm ≥		12	14
4	Foldability at low temperature °C≤		-40
5	Impermeability( 0.3Mpa, 30min)		Impermeable
6	Solids content %≥		80
7	Surface drying time, h≤		12
8	Hard drying time, h≤		24
9	Heat shrinkage %	≤	1.0
		≥	-4.0
10	Cohesive strength of moist base surface, Mpa ≥		0.50
11	Outspread aging	Heat aging	No gash or deformation
		Artificial weathering aging	No gash or deformation
12	Heat treatment	Retention rate of tensile strength %	80-150
		Elongation at break % ≥	500		400
		Foldability at low temperature°C	-35
13	Alkali treatment	Retention rate of tensile strength %	60-150
		Elongation at break % ≥	500		400
		Foldability at low temperature°C	-35
14	Acid treatment	Retention rate of tensile strength %	80-150
		Elongation at break % ≥	500		400
		Foldability at low temperature°C	-35
15	Artificial weathering aging	Retention rate of tensile strength %	80-150
		Elongation at break % ≥	500		400
		Foldability at low temperature°C	-35