Non asbestos painted fiber cement board Contin - Contin

Non asbestos painted fiber cement board Contin - details see: https://www.buildingsupplieshub.com/non-asbestos-painted-fiber-cement-board-contin-10029241

Place of Origin: Lithuania	Brand Name: Contin	Model Number: Contin	Type: Fiber Cement Boards
Size: 1220x2440x8	Certificate: CE	Density: 1,6-1,8g/cm3	Bending strenght laboratorian condition: longitudinal 26MPa, transversal 13MPa
Bending strenght wet condition: longitudinal 20MPa, transversal 10MPa	Modulus of elasticity: 14220 MPa	Fire resistance: A2 s1 d0 class	Colour: Any. For extra charge antigraffiti coating
Warranty: 30 years	Performance: Fireproof, waterproof, sound insulation

contact supplier for Non asbestos painted fiber cement board Contin

JSC „Paladija“ is offering a new type painted high density fiber cement panel „Contin“, which is made in Europe. These panels are used for exterior and interior decoration. Contin panels are made of high density fiber cement boards, which increases the resistance of environmental factors. The surface is covered by high quality polyurethane paint which microporous do not absorb water drops, but is vapour permeable. This feature withholds your facade of getting soaked, therefore any installation fault or other factor will not affect technical characteristics of panel. Your façade will remain in a perfect condition for a long time, because “Contin” panels’ surface is very tough, scratch proof and UV resistant. These panels can be easily cleaned, because surface is resistant to scrub, abrasion, disinfectants. It can also be covered by anti-graffiti coat.

All these unique features of “Contin” panel meet the highest façade decoration requirements.

Raw materials:

Quartz sand(SiO₂);

Silicate cement;

CelluloseFiber;

Al(OH)_3;

UV resistant polyurethane paint.

1.	Mechanical resistance	LST EN 12467:2012	Class 3
2.	Reaction to fire	LST EN 12467:2012	A2-s1, d0
3.	Release of dangerous substance	LST EN 12467:2012	NPD*
4.	Water permeability	LST EN 12467:2012	Impermeable
5.	Durability against warm water	LST EN 12467:2012	Category A
6.	Durability against soak/dry	LST EN 12467:2012	Category A
7.	Durability against freeze-thaw	LST EN 12467:2012	Category A
8.	Durability against heat-rain	LST EN 12467:2012	Category A
9.	Mechanical resistance	LST EN 12467:2012	Bending strength MOR: - longitudinal 26MPa transverse 13MPa Bending strength MOR in the wet condition (after 24h in water): - longitudinal 20MPa -transvers 10MPa
10.	Modulus of elasticity MOE, MPa	LST EN 12467:2012	14220
11.	Water permeability	LST EN 12467:2012	After 24h none
12.	Durability against warm water	LST EN 12467:2012	Conform (56 days )
13.	Durability against soak/dry	LST EN 12467:2012	Conform (50 cycles)
14.	Durability against freeze-thaw	LST EN 12467:2012	Conform(100 cycles)
15.	Durability against heat-rain	LST EN 12467:2012	Conform (50 cycles)
16.	Tolerances on nominal dimensions:	LST EN 12467:2012
	Max nominal lenght, mm tolerance, %	LST EN 12467:2012	2440 0
	Max nominal width tolerance s, %	LST EN 12467:2012	1220 + 0,16
	Nominal thickness, mm tolerance, %	LST EN 12467:2012	8 + 2,38
	Tolerance on straightness of edges	LST EN 12467:2012	0,0
	Tolerance on squareness of edges mm/m	LST EN 12467:2012	0,0
	Density,g/cm³	LST EN 12467:2012	1,7042
17.	Water absorption after 24h,%	LST EN ISO 10545-3	≤11%
18.	Moisture movement, %: - the longitudinal direction -transverse direction	LST EN 12467:2012	0,042, 0,022,
19.	Coefficient of thermal conductivity λ: - relative humidity 50% - relative humidity 90%	LST EN 1745:2002	0,64W/(m· K), 0,70W/(m· K),
20.	Resistance to static water impact, h degree of blistering, point	LST EN ISO 2812-2:2004; LST EN ISO 4628-2:2004	Conform, >24 Conform, 0(S0).
21.	Vapour transmission	LST EN ISO 7783:2012	Class V3
22.	Water permeability	LST EN 1062-3:2008	Class W3
23.	Hardness (Pendulum damping test),s	LST EN ISO 1522:2007	Conform, 99
24.	Resistance to scratching	LST EN 13523-4:2002	Conform, the 5H pencil-scratches are not.
25.	Adhesion to fibre-cement sheet, MPa	LST EN ISO 4624:2003	Conform, 2,5
26.	Adhesion to fibre-cement sheet,cross-cut test	LST EN ISO 2409:2007	Conform, stage 3
27.	Wet-scrub resistance of coatings - decrease in the thickness after 200 wet scrubbing cycles, μm	LST EN ISO 11998:2006	Conform,0,5
28.	Resistance to abrasion(Taber method) mg	LST ISO 7784-2:2006	Conform, 82
29.	Resistance toUV rays (after 2000 h).	DIN EN ISO 11341, cycle A	Δ E<1,5, no visible changes
30.	Resistance to static3% NaClimpact, h degree of blistering, point degree of blistering, point	LST EN ISO 2812-1:2007, A method LST EN ISO 4628-1:2006 LST EN ISO 4628-2:2004	Conform, >24; 0 (S0).
31.	Resistance to chemicals static impacts h - industrial oil - gasoline - 5% acetic acid	LST EN ISO 2812-1:2007, A method LST EN ISO 4628-1:2006 LST EN ISO 4628-2:2004	Conform, >24h 0(S0)
32.	Resistance to cleaning and disinfecting solutions for static impact - 5% soda solution- 1% dodecyldimethylammonium chloride solution - 1% chloramine-B - 0,5%TAAB 2 - isopropyl alcohol	LST EN ISO 2812-1:2007, A method LST EN ISO 4628-1:2006 LST EN ISO 4628-2:2004	Conform, >24h 0(S0)