High polymer polyethylene polypropylene composite waterproof membranes\PP+PE+PP waterproof membranes - CH-PP+PE

Several layers of macromolecule compound materials, Good durability, High broken strength, High anti-permeability - details see: https://www.buildingsupplieshub.com/high-polymer-polyethylene-polypropylene-composite-waterproof-membranes-pp-pe-pp-waterproof-membranes-10100217

Type: Waterproof Membrane	Place of Origin: Shandong China (Mainland)	Brand Name: chenhua	Model Number: CH-PP+PE
Use: waterproofing	Core material: PE,EVA	Technics: Heat synthesis	color: black ,white,green,grey etc
Width: 1.15M,1.20M,1M	Length: 100M,50M	Thickness: 0.5mm-1.5mm

$High polymer polyethylene polypropylene composite waterproof membranes\PP+PE+PP waterproof membranes$

$contact supplier for High polymer polyethylene polypropylene composite waterproof membranes\PP+PE+PP waterproof membranes$

Polyethylene polypropylene/polyester fibre waterproofing roll material

is made by multipleply different materials, especially its ageing and weathering resistance layer enables the

membrane possess more longer effective age. It can bond with many kinds of adhesions, firm and secure.

Incase of cement-base, cementitious agent can be used, the cementitious agent can easily enter into the

non-woven felt layer, forms a well-combination with cement after solidification, permanent durability.
Width: 1.15m, 1.2m Length: 50m, 100m or as request

Material: PP nonwoven laminated with PE film

This product is composed of extruded PE membrane with polypropylene fiber or Dacron covered

on both sides of the core membrane as reinforced layer to make it big friction and easy to be stuck

firmly to the concrete.Wth characteristics of easy installation,no pollution and good durability.

Material: PP nonwoven laminated with PE film

Features: good tensile strength,excellent elongation,non-toxic,no pollution

color: white.etc

weight:400g/m2

Thickness: 0.7-0.8mm

Application:

products used in roofing,basement,restroom,water conservation,warehouse to protect

structure from water.

Technical Data(GB18173.1-2006)

Items		FS2 Resins
Tensile Strength(N/cm)	Normal temperature≥	60
Elongation%	60°C≥	30
	Normal temperature≥	400
	400-20°C≥	10
Tear Strength ( N)	≥	20
No leakage(30 min)Water impermeability		0.3Mpa.
Cold bending°C≤		-20
Heating expansion amount	Expansion ≤	2
Heating expansion amount	Shrinkage ≤	4
Air oven aging (80°C×168h)	Tensile strength retention% ≥	80
Air oven aging (80°C×168h)	Glue broken elongation retention% ≥	70
Alkali resistance (10%CA(OH)2 Normal temperature×168h)	Tensile strength retention% ≥	80
Alkali resistance (10%CA(OH)2 Normal temperature×168h)	Glue broken elongation retention% ≥	80
Resistance to ozone aging (40°C×168h)200pphm		No crack
Artificial weathering	Tensile strength retention% ≥	80
Artificial weathering	Glue broken elongation retention% ≥	70