high alumina refractory cement CA50A600 - CA50A600

1. Rapid-hardening, high strength., 2. High refractoriness, high-temperature service performance. - details see: https://www.buildingsupplieshub.com/high-alumina-refractory-cement-ca50a600-10083302

Place of Origin: Henan China (Mainland)	Brand Name: TAGORE	Model Number: CA50A600	Color: Grey
Feature: Acid-Proof,Refractory	Main Raw Material: Aluminate	Type: Other	Hardening Feature: Extra Rapid Hardening
Heat of Hydration: Moderate Heat	Strength Grade(Mpa): 42.5

$high alumina refractory cement CA50A600$

$contact supplier for high alumina refractory cement CA50A600$

Features:

1. Rapid-hardening, high strength.

2. High refractoriness, high-temperature service performance.
3. Good resistance to abrasion, high wear resistance.

4. Stable hydrating capacity.

5. Good anti-corrosion performance.

6. High thermal shock stability.

Application:

1. Construction of sulfate corrosion resistance and high temperature proof.

2. Used in rush repairs, leakage stopping , resistance to sulfate attack.

3. Ideal binder for refractories such as refractory concrete, refractory castable, ramming mixing, gunning mixing and manmade marble bricks.

4. Used as ceramic adhesive.

5. Used for sealing coating products and refractory mortar.

6. Used in chemical industry, metallurgical industry, building materials.

CA50 A600	Date of Test : 13thJune,2013
Items		GB/T205-2000	Test Results
Chemical Analysis (%)	Al2O3	50-60	50.27
	SiO2	≤8.0	7.96
	Fe2O3	≤2.5	2.18
	R2O	≤0.40	0.37
	S	≤0.1 GB201-2000	-
	Cl	≤0.1 GB201-2000	-
		GB201-2000
Finess	0.045 sieve residue %	≤20	17.9
Finess	Specific area m2/kg*	≥300 GB/T8074	324
Setting Time (min)	Initial	≥30	188
Setting Time (min)	Finial	≤360	256
Flexural Strength (Mpa)	1 day	≥5.5	5.9
Flexural Strength (Mpa)	3 days	≥6.5	6.8
Compression Strength (Mpa)	1 day	≥40	45.3
Compression Strength (Mpa)	3 days	≥50	58.5