CE quality perfect waterproofing performance widely used in construction bentonite geosynthetic clay liner - GCL-NP/GCL-OF

Bentonite geosynthetic clayliner, 1 Three layers, 2 Used below zero, 3 Suit uneven settlement, 4 Meet ISO9001 CE ASTM - details see: https://www.buildingsupplieshub.com/ce-quality-perfect-waterproofing-performance-widely-used-in-construction-bentonite-geosynthetic-clay-liner-10100283

Type: Other Waterproofing Materials	Place of Origin: Jilin China (Mainland)	Brand Name: LiuFangzi or OEM	Model Number: GCL-NP/GCL-OF
peel strength (N/100mm): 70 or 69	tensile strength(N/100mm): 879 or 1114	methylene volume(g/100g): 32	Hydrostatic Pressure: 0.4(or 0.6)MPa, 1h, no leakage
Specification: 4.5 to 5.8kg/m2	Tensile Strength: 879N/100mm or 1114N/100mm	Breaking Elongation: 10.6%	Watertightness: 3.910-11 m/sec or 3.910-11 m/sec
Size: 6m*30m	Material: bentonite

Bentonite geosynthetic clay liner

Natural sodium bentonite Geosynthetic clay liner GCL - NP without high density

polyethylene HDPE
Testing by national Research Center of Testing Techniques for Building Materials.

Detection basis: the standard technolog of waterproof system of beijing's New line's

Metro
Testing no. : 2010A00242
Testing time: April 1 ,2010
Note: 1. the thickness of GCL torlance≤15%
2.The torlance of sodium bentonite pellet in unit area is ±0.5KG/M2

No.	Properties	Unit	Test standard	Testing standard data	Test result
1	Bentonite Swell Index	ml/2g	ASTM D5890-2002	≥24	24
2	Bentonite Fluid Loss	ml	ASTM D5891-2002	≤18	15
3	GCL Tensile Strength	N/cm	ASTM D6768-2004	≥60	103
4	GCL Peel Strength	m/s	ASTM D6496-2004	≥400	709
5	Bentonite Moisture	%	ASTM D4643-2008	12%	9%
6	GCL Hydraulic Conductivity	m/s	ASTM D5887-1999	3.9 x 10^-11	3.9 x 10^-11
7	GCL Index Flux	m3/m2/s		5.8 x 10^-9	5.8 x 10^-9
8	GCL Bentonite Mass Per Unit Area	g/m2	ASTM D5993-1999	≥4000 toerlance ±0.5KG/M2	4500
9	Non woven Geotextile Mass Per Unit Area	g/m2	ASTM D5261-1992	206	206
10	Woven Geotextile Mass Per Unit Area	g/m2		111	111
11	GCL Internal Hydrated Shear Strength	kpa	ASTM D6243-2006	26	26
12	Assay of Natural Sodium Bentonite		XRD. Ph anion	Natural Sodium Bentonite	Natural Sodium Bentonite

The advantage of Liufangzi GCL

1. Environment friendly

Liu Fangzi GCL is made of natural raw materials of sodium-bentonite.It is raw and natural materials,;aging and corrosion seldom happen. It can keep its quality and then it does not cause any injuries and pollution for human and the environment. It is not only waterproof, but also has good ventilation performance. It can stick up for the exchange of the ecological environment. It is a pure natural, new, green waterproof material

2. Permanent waterproof, excellent performance

Natural sodium bentonite was formed billions of years ago.

Its waterproof properties are much more durable than that of the buildings. Sodium bentonite would transform to high density septum under hydro pressure.

3. Easy to construct

Bentonite powder, nails and washers are enough for connection and fixation. Construction is not constrained by weather conditions and it could be taken under cold or wet conditions. Bentonite powder is spread on overlap point.

4. Strong Self-Restore Capacity

The integration between waterproof material and its target enables GCL a 20~28 times swelling volume. Even if concrete structure trembles or subsides, the bentonite in GCL would restore the crack of 2mm or below on the concrete structure immediately. Even if the diameter of perforation reaches 30 mm, the restoration will be finished within 15 days completely.

Packaging Detail:Poly bags (negotiable) One 20FC loads about 3800 square meters.

Delivery Detail:within 10 days (negotiable)