CCE.FIRE refractory fire-resistant brick - SK 36

1.Professional refractory brick manufacturer, 2.Al2O3:42-80%, 3.Common size:230x114x65/75mm, 4.45 years production experience - details see: https://www.buildingsupplieshub.com/cce-fire-refractory-fire-resistant-brick-10082097

Place of Origin: Shandong China (Mainland)	Brand Name: CCE,FIRE	Model Number: SK 36	Size: 23011465mm/75mm
Type:: SK32,SK34, SK35, SK36,SK37,SK38	Refractoriness: 1770C	Porosity(%): 23%	Cold crushing strength: 40Mpa
AL2O3+SiO2: 95%	Fe2O3: 2.4%	The third inspection: SGS	Certificate: TUV,BV,ISO9001
Standard: ASTM,JIS	Packing: wooden pallet

$CCE.FIRE refractory fire-resistant brick$

$contact supplier for CCE.FIRE refractory fire-resistant brick$

Products Description

CCEFIRERefractorybrick is dense shaped refractory material. With high refractoriness and mechanical behavior under high temperature, refractory brick is the necessary material of high-temperature services, mainly used for industrial furnaces and kilns and thermal equipment.
Refractory brick has wide applications, mainly used in metallurgy, construction(cement and glass), petroleum, chemical industry, electric power and machine building.

All kinds of refractory fire brick can provide.

Item	Refractory fire brick
Types	High Alumina Brick for Hot-blast Stove Creep Resistant High Alumina Brick Creep Resistant Clay Brick Fire Brick for Hot-blast Stove Combined Brick for Hot-blast Stove
Sizes:	Common size:230x114x75/65mm Also supplyspecial shaped according to your drawing
Characteristic	1.low creep deformation 2.huge heat capacity 3.great refractoriness 4.thermal shock resistance
Package	wooden pallet with shrinkage film,paper protect angle.

Products Details

Quality Control

1.Supply Lab report for each shipment.

2.The third inspection (SGS) can available.

Production Range

Technical data

Items/ Type No.	RL-65	RL-55	RL-48		RL-70	DRL-75		DRL-80
AL₂O₃%	≥65	≥55	≥48		≥70	≥75		≥80
refractoriness, no less than	1790	1770	1750		1790	1790		1790
Refractoriness under Load(0.2 MPa)	≥1500	≥1470	≥1420		≥1500	≥1550		≥1650
Linear Change on Reheating(%)	1500°C×2h +0.1 -- -0.4	1500°C×2h +0.1 -- -0.4	1450°C×2h +0.1 -- -0.4		1450°C×2h +0.1 -- -0.2	1500°C×2h +0.1 -- -0.2		1500°C×2h +0.1 -- -0.2
Apparent Porosity(%)	≤24	≤24	≤24		≤21	≤20		≤19
Cold Crushing Strength (Mpa)	49	44	39		60	65		70
Creep Property High Temp				≤0.6 (1350°C×50h)		≤0.6 (1450°C×50h)	≤0.6 (1500°C×50h)

SK series refractory brick

Item	Fireclay Brick		High Alumina Brick
Item	SK32	SK34	SK35	SK36	SK37	SK38
Al2O3 (%) ≥	38	42	48	55	65	75
Refractoriness (oC) ≥	1670	1730	1750	1770	1790	1810
Refractoriness under Load (oC) ≥	1250	1300	1420	1470	1500	1520
Linear Change (%) (2h)	1350 oC	1350 oC	1450 oC	1500 oC	1500 oC	1500 oC
Linear Change (%) (2h)	-0.5	-0.5	-0.4-+0.1	-0.4-+0.1	-0.4-+0.1	-0.4-+0.1
Porosity (%) ≤	26	26	22	22	23	23
Cold Crushing Strength, MPa ≥	15	20	39.2	44.1	49	53.9